not one for me sorry, I would get the coating removed,
G
Smashed supercharger; what to do next?
-
- Site Admin
- Posts: 5039
- Joined: June 18th, 2006, 9:31 am
- Location: Bedford, UK
- Contact:
Re: Smashed supercharger; what to do next?
Guy Croft, owner
-
- Posts: 13
- Joined: May 9th, 2012, 12:03 pm
Re: Smashed supercharger; what to do next?
Interesting answer, Guy. Not to question your judgement, but would you mind you elaborating on your reasons, please? How would you propose removing the coating?Guy Croft wrote:not one for me sorry, I would get the coating removed,
G
Chris
-
- Site Admin
- Posts: 5039
- Joined: June 18th, 2006, 9:31 am
- Location: Bedford, UK
- Contact:
Re: Smashed supercharger; what to do next?
There are solvents that will dissolve teflon - which is what it will be, contact
10 Christleton Court
Manor Park
Runcorn
Cheshire
WA7 1ST
United Kingdom
Phone:+44 (0)1928 571000
Fax:+44 (0)1928 571010
Web:www.whitfordww.com
Yours are coated by robot at mfr and the layer thickness done manually would be impossible to assure. It is very easy to overcoat and the rotors won't turn at all, even with a simple figure 8 Roots blower. Moreover my conductive nickel-polymer needs baking at 220 deg and the rotors will almost certainly 'morph' at that temperature...
Would not be fun to do and render scrap, would it?!
G
10 Christleton Court
Manor Park
Runcorn
Cheshire
WA7 1ST
United Kingdom
Phone:+44 (0)1928 571000
Fax:+44 (0)1928 571010
Web:www.whitfordww.com
Yours are coated by robot at mfr and the layer thickness done manually would be impossible to assure. It is very easy to overcoat and the rotors won't turn at all, even with a simple figure 8 Roots blower. Moreover my conductive nickel-polymer needs baking at 220 deg and the rotors will almost certainly 'morph' at that temperature...
Would not be fun to do and render scrap, would it?!
G
Guy Croft, owner
-
- Posts: 13
- Joined: May 9th, 2012, 12:03 pm
Re: Smashed supercharger; what to do next?
Thanks Guy. I've read all sorts about what they're coated with. I'd always thought it was Teflon, but then I read that it was just regular powder coat. It certainly seems Teflon-like to me but then this is the first 'charger I've taken apart.
Thanks for explaining why your coating would be no good.
I will drop the company you mention a line, it sounds like having it all stripped off is the most sensible idea.
Chris
Thanks for explaining why your coating would be no good.
I will drop the company you mention a line, it sounds like having it all stripped off is the most sensible idea.
Chris